In fact, the spearhead is otherwise pointed out! Since no matter what the origin of the stainless steel material is, whether it is 201 or 304, the rust problem occurs after the matte finish and the rose gold plating. That ruled out the problem of J3 replacing J1, but the key cleaning steps have been repeatedly tested, or the same result, then which process of the process will be flawed? It is understood that titanium and rose gold are the same For a furnace body, the entire materials and process flow are the same, there will be no other major differences, but the cost will be different. However, precisely because of this, the quality problems faced by the rose gold and titanium gold products are also more explosive. It is probably the reason of the raw materials for color plating. Because so many possibilities are ruled out, we found that the only raw materials used in the color plating are the only things we cannot control. There are only three or two suppliers in Foshan. Everyone takes the same place and materials, so all manufacturers who make rose gold or titanium gold, no matter who you do, how careful, what furnace and raw materials, will Facing the same problem... How to avoid rusting after rose gold plating? It is understood that manufacturers will suggest or request a fingerprint-free process when making rose gold technology for customers, so that the rusting phenomenon is largely avoided. occur. "If the customer is not willing to do fingerprintless, sometimes in order to avoid trouble, we would rather send this process, although the cost has increased" "Rose Gold has been rusted, has not changed over the years, there have been many previous complaints But it has been dealt with without complaints and must be fingerprint-free," said a senior person who has been engaged in the industry for many years. Finally, we have returned to the focus of yesterday’s business feedback reports. In today’s communication, there are indeed manufacturers who have expressed their views on the material itself. The material itself can't be said that it has nothing to do with it. Over the years, the quality of stainless steel sheet has felt a decline. For example, the peeling line on the 2B board is not visible on your surface. It may be covered by the last layer of passivation. The peeling point or trachoma point appears after frosting or drawing. After the rose gold plating, the line point changes The white part is easy to rust, which may be related to the material of the stainless steel blank. Today, the industry's heated discussion on this issue has indeed exceeded the editor's expectations, but this just confirms the stainless steel decoration industry's pursuit of process innovation and quality improvement in recent years. Today, when we can think of solving problems without fingerprints: tomorrow, we can find out the crux of the problem and break through the difficulties of the process. This is the charm of the stainless steel decoration industry!